PROMAX supplies wax and amides for extrusion, moulding, paint, ink, rubber, lubricants and hardening agents.
Ceras y Amigas
Especificación
| Product | Trade name | Melting point | Acid value(mgKOH/g) | Color(Gardner) | Form | Application |
| Wax | ||||||
| Polyethylene wax | PRO WAX 1 | 96-100 drop point | 1 max. | solid | Extrusion of rigid or soft PVC. External lubricant with low amount of filler. Gives good surface shine. | |
| Polyethylene wax | PRO WAX 2 | 110-120 | 2 max. | solid | Extrusion of soft or rigid PVC. Giving rigid shine surface. | |
| Polyethylene wax | PRO WAX 3 | 90-110 | 3 max. | solid | Extrusion and injection of rigid or soft PVC. Also for rubber and PE with high molecular weight. | |
| Paraffinic compound | PRO WAX 4 | 90-100 | ivory | solid | Extrusion of PVC rubber and other primary products. Helping pigment dispersion in particular with rubber. | |
| Paraffinic compound | PRO WAX 5 | 5 max. | liquid | Basically external but has good compatibility with PVC resins. Shiny finishes without exudation. Soft PVC lubricant for cable coverings. | ||
| Polyethylene wax | PRO WAX 6 | 78-82 | 2 max. | solid | Rigid PVC extrusion. Gives good shine. Non- transparent rigid polymers. | |
| Amidas | ||||||
| Fatty amide | PRO AMIDAS 1 | 140-145 | 10 max. | beads | Anti-static and pigment dispersion agent. Hardening agent for paints lacquers asphalts etc. In PVC used for calendering or blown film extrusion. Lubricant for ABS polystyrene acryrene acrylnitrile styrene polystyrene and polipropilene pigment dispersion agent. | |
| Fatty amide | PRO AMIDAS 2 | 140-145 | 10 max. | powder | Anti-static and pigment dispersion agent. Hardening agent for paints lacquers asphalts etc. In PVC used for calendering or blown film extrusion. Lubricant for ABS polystyrene acryrene acrylnitrile styrene polystyrene and polipropilene pigment dispersion agent. | |
| Esters | ||||||
| Fatty acid ester | PRO ESTER 1 | 16-20 freezing point | 2 max. | 1 max. | liquid | Secondary lubricant and plastifier in all types of thermoplastic. Gives smooth surface and shine to PVC. Good transparency. |
| Carboxilic fatty acid | PRO ESTER 2 | 44-46 | 2 max. | 1 max. | solid | Act as fluidifier in rigid PVC. Greatly used when working at high temperatures. |
| Fatty acid ester | PRO ESTER 3 | 51-58 | 3 max. | 2 max. | solid | Injection and extrusion of rigid PVC. In rigid pipes with high mechanical resistance. |
| Fatty acid ester | PRO ESTER 4 | 2 max. | 2 max. | liquid | Calendering not sticky. Extrusion and injection of soft PVC. Bottle- making. | |
| Stearilic phthalate | PRO ESTER 5 | 52-54 | 7 max. | solid | Act as a fluidifier in rigid PVC. Recommended when working at high temperatures. | |
| Sebacate diisotridecyl | PRO ESTER 6 | Inf.0° | 1 max. | liquid | PVC plasticier. Recommended when working at high temperatures. | |
| Isooctyl sterate | PRO ESTER 7 | 12-15 freezing point | 1 max. | 2 max. | liquid | Textile lubricant used on synthetic fibres. |
| Alcohols | ||||||
| Fatty Aalcohols | PRO ALCOHOLS | 49-56 | 1 max. | solid | Internal lubricant for both rigid and soft PVC. Especially recommended in rigid PVC. Compatible with organic tin compounds (calendering and bottle making). | |
| Polialcohol esters | ||||||
| Fatty acid ester of polyalcohol | PRO ESTER 8 | 54-64 | 3 max. | 1 max. | solid | Rigid PVC extrusion. Improves flow. Alimentary use. |
| Glycerol monosterate | PRO ESTER 9 | 56-60 | 3 max. | 3 max. | solid | Rigid PVC extrusion. Improves flow. Alimentary use. |
| Polyalcohol ester | PRO ESTER 10 | 10 max. Freezing point | 4 max. | 75-85 | liquid | Basically for rigid PVC. Good light stability. Alimentary use. |
| Polyalcohol ester | PRO ESTER 11 | 48-52 | 2 max. | 1 max. | Rigid PVC extrusion. Alimentary use. | |
| Polyalcohol ester | PRO ESTER 12 | 56-62 | 3 max. | 1 max. | solid | Injection extrusion and blowing of rigid PVC and transparents. |
| Polyalcohol ester | PRO ESTER 13 | 60-73 | 3 max. | solid | Extrusion and blowing principally in non-toxic bottle-making. Good transparency. | |
| Pentaeritrite ester | PRO ESTER 14 | 48-52 drop point | 2 max. | 1 max. | solid | Injection extrusion and blowing of rigid PVC and transparents. |
| Compound esters | ||||||
| Compound ester | PRO ESTER 15 | 92-102 | 1 max. | solid | Extrusion of rigid PVC. Recommended for formulations with high amounts of filler. Does not give problems of exudation. | |
| Saponified compound ester | PRO ESTER 16 | 110-115 | 15 max. | 2 max. | solid | Extrusion and blowing of rigid PVC. Widely used in bottle-making. Limited uses in soft PVC. |
| Partially saponified ester | PRO ESTER 17 | 95-105 | 5 max. | solid | Improves the flow of rubber mixtures. Demoulding agent. Activates vulcanization in sulphur-based systems. | |
| Polyalcohol compound ester | PRO ESTER 18 | 68-72 | 3 max. | 5 max. | solid | Extrusion of rigid profile and blowing of hollow bodies. |
| Metallic salt of fatty acid | ||||||
| Fatty acid salt | PRO SALT 1 | 146-166 | 4 max. | solid | ||
| Fatty acid zinc salt | PRO SALT 2 | 95-105 | solid | Process lubricant for natural and synthetic rubber. | ||
| Complex esters | ||||||
| Complex esters | PRO ESTER 19 | 15 max. | 1 max. | beads | Anti-sticking agent in calendering. Used in both rigid and transparent calendered rigid PVC. | |
| Complex esters | PRO ESTER 20 | 53-59 | 15 max. | 1 max. | beads | Calendering of transparent rigid films. Blown bottle extrusion. |
| Complex esters | PRO ESTER 21 | 10 max. | 50-60 | liquid | General soft and rigid PVC. Good demoulding agent. | |
| Complex esters | PRO ESTER 23 | beads | Anti-sticking agent in calendering. Used in both rigid and transparent calendering rigid PVC. | |||
| Base AOP | General soft and rigid PVC. Good demoulding agent. | |||||